X10CrAlSi13 1.4724 BS-EN-10095-1999

Steel designation

NameX10CrAlSi13

Number1.4724

 Chemical composition

C:max.0.12

Si:0.70~1.40

Mn(max):1.00

P(max):0.04

S(max):0.015

Cr:12~14

Al:0.70~1.20

X10CrAlSi13 1.4724 Mechanical properties at room temperature

Form: flat products

Thickness a or diameter(d:mm): a ≤ 12

HB max.:192

Proof strength: Rp0,2N/mm2(min):250

Tensile strength :Rm N/mm2:450~650

A % min:

Long product:15

Flat products:(1)0,5≤a<3:(1,tr):13   (2)3 < a  (1):15;   (tr):15

X10CrAlSi13 1.4724 Heat treatment

Symbol:+A (A = annealed)

Temperature(℃): 800~860

Type of cooling:  air, water, In special cases furnace cooling is also permitted

Maximum application temperature Ta for air

Ta max(℃): 850

(The loss of metal caused by scaling does not exceed 1 g/m2⋅h at Ta, and does not exceed 2 g/m2 at Ta + 50 ℃ on average for a period of 120 h with four intermediate coolings.)

 

Creep properties

Estimated average value of the strength for 1 % elongation at elevated temperature (Strength in N/mm2)

Elongation 1 % in 1 000 h:

500℃:80

600℃:27.5

700℃:8.5

800℃:3.7

900℃:1.8

Elongation 1 % in 10 000 h:

500℃:50

600℃:17.5

700℃:4.7

800℃:2.1

900℃:1.0

 

Estimated average value of the strength for rupture at elevated temperature

(Strength in N/mm2)

       Rupture in 1 000 h:

500℃:160

600℃:55

700℃:17

800℃:7.5

900℃:3.6

Rupture in 10 000 h:

500℃:100

600℃:35

700℃:9.5

800℃:4.3

900℃:1.9

Rupture in 100 000 h:

500℃:55

600℃:20

700℃:5

800℃:2.3

900℃:1.0

Physical properties for the steels and nickel alloys

Density(kg/dm2):7.7

Linear expansion coefficient (10⁻⁶K⁻¹): between 20℃ and

200℃:10.5

400℃:11.5

600℃:12.0

800℃:12.5

1000℃:-

Thermal conductivity

W/(m.K)

      at 20℃: 21

at 500℃:23

 

Specific heat capacity

kJ(kg.k)

        at 20℃:0.50

 

  Electrical resistivity

             Ω.mm²/m

       at 20℃:0.75

 Magnetizability:yes